XPS surface analysis

X-ray photoelectron spectroscopy (XPS) is a surface analysis technique that provides quantitative elemental and chemical state information about the top layers of a material.

 

XPS is essential for understanding the interface between electrolytes and electrodes. Cathode and anode materials of Li-ion cells can be studied to confirm post-cycling changes in composition, to understand changes in the chemistry of the electrode components, and to determine how the solid electrolyte interface (SEI) layer varies in depth as it develops. XPS has proved useful in studying surface pre-treatment of graphite electrode materials to significantly slow the irreversible consumption of material during battery charging. Surface analysis tools from Thermo Fisher Scientific have all the features required for battery material analysis, including vacuum transfer modules for safe transport of sensitive battery samples from a glove box to the instrument without exposure to ambient atmosphere.

XPS sample data for battery components

NMC cathode surface profile before and after cycling

Cathode materials like lithium, nickel, manganese, cobalt (NMC), and oxygen change in stoichiometry depending on whether the cell is charged or discharged. In this experiment, two NMC cathode samples were profiled on the Thermo Scientific K-Alpha XPS system. One sample was taken from a pristine, unused cell, while the other was from a cell that had been through several charge/discharge cycles and was in a charged state when the cell was disassembled. Because lithium is highly sensitive to air and moisture, the electrode materials were loaded into the K-Alpha Vacuum Transfer Module (VTM) in a glove box for transport to the XPS system.

 

The survey spectra (left figure) show peaks for the cathode materials (Li, Ni, Mn, Co, O) and the binder medium (F and oxygen-containing polymers) that holds the materials together. In the pristine sample (green), the binder is evident as a significant amount of residue on the surface. This could be important during the first use of the cathode, if the binder residue is mobile in the electrolyte or reacts to begin the formation of a surface layer that impedes ion transport. The cycled cathode (red) still shows the presence of the binder as well as residue from the electrolyte at the surface.

Surface profile of NMC cathode before and after cycling. (left) Survey spectra from the pristine (green) and cycled (red) cathode samples showing evidence of cathode materials and binder. (right) Atomic percentages of NMC components from pristine vs cycled samples. Mn, Co, and Ni intensities remained stable after cycling while Li decreased due to the charged state of the cycled battery.

Comparing the NMC components (excluding oxygen) between the two samples (right figure), the relative intensities of Ni, Mn, and Co were similar. However, the amount of Li detected in the cycled cathode was around 40% of that observed in the pristine cathode. This was expected in a sample from a charged cell, where the Li ions have transported toward the anode, depleting the lithium level in the cathode.

Depth profile of LiPON solid electrolyte

XPS depth profile of LiPON solid electrolyte

 

Depth profiling analysis of the lithium phosphorus oxynitride (LiPON) solid electrolyte can help you understand the stoichiometry of the film as a function of depth. The 1 keV monatomic Ar+ ion profile (left) induces Li “pile-up” at the interface because the monatomic ion beam induces Li mobility in the sample. Using a cluster ion source, such as the Thermo Scientific MAGCIS ion source, prevents this from happening, resulting in an accurate measurement of the composition of the electrolyte film.


X-ray photoelectron spectroscopy use cases in battery research and manufacturing


X-ray photoelectron spectroscopy instruments

Thermo Scientific K-Alpha XPS

High-resolution XPS with a fast, efficient, automated workflow. Includes ion source for depth profiling.

Thermo Scientific Nexsa G2 XPS

Micro-focus X-ray source paired with innovative multi-technique options. A dual-mode ion source is available for monoatomic and cluster ion depth profiling.

Thermo Scientific ESCALAB QXi XPS

High-resolution XPS with additional sample preparation options. A dual-mode ion source is available for monoatomic and cluster ion depth profiling.


X-ray photoelectron spectroscopy resources for batteries

X-ray photoelectron spectroscopy documentation and literature

XPS battery application notes

">